3 vhb adhesive transfer tapes with adhesive 100mp f9460pc F9469PC f9473pc product description 3m vhb adhesive transfer tapes f9460pc, F9469PC and f9473pc utilize the high performance of 3m adhesive 100mp, which has excellent long term holding power with much higher adhesion strength than typical pressure sensitive adhesive systems. these vhb adhesive transfer tapes are transparent and are ideal for use in many interior and exterior industrial applications to replace rivets, spot welds, liquid adhesives, and other permanent fasteners. construction technical data april, 2005 products 3m vhb adhesive transfer tapes f9460pc F9469PC f9473pc adhesive thickness 0.002 in. 0.005 in. 0.010 in. (0.05 mm) (0.13 mm) (0.26 mm) liner material 58# polycoated kraft 0.004 in. (0.10 mm) products 3m vhb adhesive transfer tapes f9460pc F9469PC f9473pc thermal coefficient of expansion 770 x 10 -6 mm/mm/? thermal conductivity (astm c-177) 0.092 btu-ft/ft 2 hr ? (0.0016 watts/cm ?) dielectric strength 23? 125? 175? 23? 125? 175? 23? 125? 175? (volts per astm d-149-97a) 1200 1000 1000 3000 2600 1900 5500 n/a n/a insulation resistance (astm d-1000) > 1 x 10 6 megaohms/in 2 density 0.04 lb/in 3 (0.98 g/cm 3 ) electrical and thermal properties note: the following technical information and data should be considered representative or typical only, and should not be used for specification purposes.
3m vhb adhesive transfer tapes with adhesive 100mp f9460pc ?F9469PC ?f9473pc - 2 - performance characteristics note: the following technical information and data should be considered representative or typical only, and should not be used for specification purposes. these vhb adhesive transfer tapes are made from the same adhesive system and are thermoplastic in nature, becoming softer as temperature increases and firmer as temperature decreases. as the adhesive becomes firmer, the adhesion performance generally increases. at low temperatures (lower than -40? [-40?]), the vhb adhesive transfer tapes become very firm and glassy; the ability to absorb impact energy is reduced. in contrast, adhesion strength reduces with increasing temperatures. typical adhesive strength properties at room temperatures are shown below. products 3m vhb adhesive transfer tapes f9460pc F9469PC f9473pc peel adhesion to 7.0 lb./in. 8.0 lb./in. 9.0 lb./in. stainless steel (120 n/10 cm) (140 n/10 cm) (160 n/10 cm) (astm d3330) normal tensile to 100 lb./in. 2 100 lb./in. 2 100 lb./in. 2 aluminum (t-block) (690 kpa) (690 kpa) (690 kpa) (astm d-897) static shear or will hold 1000 grams of loading with a time period of more than shear holding power 10,000 minutes at temperatures up to 300? (149?). to stainless steel (astm d-3654) dynamic shear to 80 lb./in. 2 80 lb./in. 2 80 lb./in. 2 stainless steel (550 kpa) (550 kpa) (550 kpa) (astm d-1002) temperature tolerance 500? (260?): 4-hour conditioning at the indicated temperature with (short term) 100 g static load. temperature tolerance 300? (149?): maximum temperature where tape supports 250 g in (long term) static shear for 10,000 minutes. solvent resistance no apparent degradation when exposed to splash testing of many (3 splash testing cycles: common solvents and fluids including gasoline, jp-4 fuel, mineral 20 seconds submersion, spirits, motor oil, ammonia cleaner, acetone and methyl ethyl ketone. & 20 seconds air dry.) uv resistance excellent uv resistance through outdoor weathering tests and weather-o-meter tests. dynamic mechanical properties note: the following technical information and data should be considered representative or typical only, and should not be used for specification purposes. for engineers who have to use adhesive properties for modeling and analysis purpose, we suggest a young s modulus of 4.5 x 10 2 kpa (measured at 23? & 1 hz) and a poisson s ratio of 0.499. for detailed adhesive modulus and damping properties, please refer to the nomograph for 3m vhb adhesive transfer tapes, which is available upon request through our technical service group. the nomograph presents adhesive modulus and damping properties as functions of temperature and frequency.
- 3 - 3m vhb adhesive transfer tapes with adhesive 100mp f9460pc ?F9469PC ?f9473pc ul 746c listings (file mh 17478) and durability testing 3m adhesive 100mp has ul 746c listings with different temperature ratings on many commonly used substrate materials as indicated in the table below. qualification for this listing requires high strength retention after extended exposure to high temperatures, humidity, cold, and cyclic conditions. substrates temperature rating stainless steel, glass/epoxy, enameled steel, ceramic, phenolic; 110? nickel plated steel (3m adhesive transfer tape F9469PC only) abs, polycarbonate, aluminum, galvanized steel 90? unplasticized pvc 75? our testing has shown that 3m adhesive 100mp yielded 92% retention of peel adhesion after the roll was aged for more than 5 years at an elevated temperature of 150? (65?). the initial tack and liner release properties were still excellent. this testing result suggests that the tape is relatively unaffected by long-term exposure to elevated temperatures. bonds made with 3m adhesive 100mp can tolerate periodic short-term exposures to temperatures up to 500? (260?). 3m adhesive 100mp is thermoplastic in nature, becoming softer as temperature increases and firmer as temperature decreases. as the adhesive becomes firmer, the performance generally increases. this performance increase is demonstrated graphically in figure 1 for 3m vhb adhesive transfer tape f9473pc. it shows the breakaway and peel forces as a function of temperature. the exception of the performance increase is at very low temperatures when high impact stresses along with high frequencies are encountered. at low temperatures, the tape becomes very firm and glassy; the ability to absorb impact energy is reduced. 100 90 80 70 60 50 40 30 20 10 0 -65 -20 020 70 temperature f force (lbs./inch width) break away peel figure 1. t-peel performance vs. temperature (3m vhb adhesive transfer tape f9473pc on aluminum) products 3m vhb adhesive transfer tapes f9460pc F9469PC f9473pc tml (%) 0.85 1.29 1.23 vcm (%) 0.00 0.02 0.01 weight loss and outgassing performance note: the following technical information and data should be considered representative or typical only, and should not be used for specification purposes. the testing was done per astm e595-77/84/90 as indicated in the nasa reference publication 1124, revision 4, ?utgassing data for selecting spacecraft materials? june 1997. the results are reported as percentage of total mass loss (tml) and percentage of volatile condensible materials (vcm), respectively, as shown below.
3m vhb adhesive transfer tapes with adhesive 100mp f9460pc ?F9469PC ?f9473pc application techniques bond strength is dependent upon the amount of adhesive-to-surface contact developed. firm application pressure helps develop better adhesive contact and improve bond strength. to obtain optimum adhesion, the bonding surfaces must be clean, dry, and well unified. some typical surface cleaning solvents are isopropyl alcohol/water mixture or heptane. * ideal tape application temperature range is 70? to 100? (21? to 38?). initial tape application to surfaces at temperatures below 50? (10?) is not recommended because the adhesive becomes too firm to adhere readily. however, once properly applied, low temperature holding is generally satisfactory. *note: be sure to follow the manufacturer s precautions and directions for use when using solvents. available roll lengths (subject to minimum order requirements): standard 60 yd. (55 m) maximum in: 1/4 in. to 3/8 in. wide 60 yd. (55 m) 3/8 in. to 1 in. wide 240 yd. (220 m) 1 in. up to 3 in. 360 yd. (330 m) 3 in. and wider 360 yd. (330 m) normal slitting tolerance 1/32 in. (0.8 mm) available sizes - 4 - storage store in original cartons at 70? (21?) and 50% relative humidity. shelf life if stored under proper conditions, products retain their performance and properties for 24 months from date of manufacture. if the products have been exposed to severe weather conditions, we suggest to precondition the products at the above storage conditions for at least 24 hours before using them. all statements, technical information and recommendations contained in this document are based upon tests or experience that 3m believes are reliable. however, many factors beyond 3m s control can affect the use and performance of a 3m product in a particular application, including the conditions under which the product is used and the time and environmental conditions in which the product is expected to perform. since these factors are uniquely within the user s knowledge and control, it is essential that the user evaluate the 3m product to determine whether it is fit for a particular purpose and suitable for the user s method of application. product use printed in u.s.a. ?3m 2005 70-0711-1387-5 (4/05) recycled paper 40% pre-consumer 10% post-consumer 3 industrial business converter markets industrial adhesives and tapes division 3m center, building 21-1w-10, 900 bush avenue st. paul, mn 55144-1000 800-223-7427 ?651-778-4244 (fax) www.3m.com/converter 3m warrants for 24 months from the date of manufacture that 3m vhb tape will be free of defects in material and manufacture. 3m makes no other warranties, express or implied, including but not limited to, any implied warranty of merchantability or fitness for a particular purpose. this limited warranty does not cover damage resulting from the use or inability to use 3m vhb tape due to misuse, workmanship in application, or application or storage not in accordance with 3m recommended procedures. limited warranty if the 3m vhb tape is proved to be defective within the warranty period stated above. the exclusive remedy, at 3m s option, shall be to refund the purchase price of or to repair or replace the defective 3m vhb tape. 3m shall not otherwise be liable for loss or damages, whether direct, indirect, special, incidental, or consequential, regardless of the legal theory asserted, including negligence, warranty, or strict liability. limitation of remedies and liability this industrial adhesives and tapes division product was manufactured under a 3m quality system registered to iso 9001: 2000 stan dards. iso 9001:2000
|
